125 Ceramic Wearing Compound


Rezorect 125 Ceramic Wearing Compound is a trowel-applied, highly abrasion resistant compound, designed to give maximum abrasion resistance in intermediate service. 125 Ceramic Wearing Compound protects against cavitation, entrained particulate abrasion, and wearing surface abrasion. It possesses maximum loading of specially sized and treated ceramic particles and silicon carbide.

The combination of the ceramic reinforcement and silicon carbide, with the corrosion resistant epoxy resin alloy, offers maximum performance in the areas of abrasion, friction reduction and turn-around time.

While 125 Ceramic Wearing Compound is designed to be cured at ambient temperature, when practical, it may be post cured by several methods to accelerate complete cure, thus placing coated objects in service in a much shorter time.

The non-sagging, non-shrinking properties of 125 Ceramic Wearing Compound permits application to vertical surfaces, cavities and intricate parts. When cured, it may be machined with tungsten carbide or diamond tools.


  • Only the highest quality resins and reinforcements are used to produce Rezorect materials, assuring the applicator of long lasting successful applications, when correctly applied.
  • Will not sag or run when applied to vertical surfaces.
  • 100% solids and will not shrink.
  • When used for non-corrosion service, single coat applications are possible.
  • Specially treated and sized ceramic reinforcements create a smooth and continuous surface.
  • User friendly 125 Ceramic Wearing Compound is easy to mix and apply, reducing application time and returning equipment to service with shorter turnaround.
  • Superior chemical resistance to 98% sulfuric acid, 50% caustic soda and many other environments offers the broadest protection.
  • Advanced adhesion properties assures long lasting protection without fear of undercutting or delamination.


  • Hoppers
  • Bins
  • Chutes
  • Pump Volutes
  • Cooling Water Pumps
  • Valves
  • Slurry Equipment
  • Mix Tanks
  • Condensers
  • Water Boxes
  • Jigs
  • Pump Rotating Elements
  • Pipe
  • Pipe Fittings
  • Scrubbers
  • Filters
  • Discharge Doors
  • Cone Bottoms
  • Shakes
  • Conveyers
  • Spiral Separators
  • Flotation Cells

TECHNICAL DATA (simplified)

ComponentsTwo (2)
Curing MechanismChemical Reaction
Sag Resistance@ 24C(75F)by 12mm(1/2 in)Thickness--No Sag
Theoretical Coverage@ 6mm(250 mils) --.16m2/ ltr. (7 ft2/gal)
Volume Solids100%
Service Temperature Limits93C(200F)Immersed 177C(350F) Dry
Flash Point>93C(200F)
Compressive StrengthASTM D-695 1110Kg/Cm2 (15,800psi)
Flexural StrengthASTM D-790 570Kg/Cm2 (8100psi)
Tensile StrengthASTM D-638 260Kg/Cm2 (3700psi)
Abrasive ResistanceASTM-D 4060 1000 Cycles, 1000 Grm load, CS/10 wheel, Taber abraser, 123 mg wgt loss
Adhesive Tensile ShearASTM D-1002 Steel 182Kg/Cm2 (2600psi)
Concrete - Concrete Failure

Contact Rezorect
United States
Jacksonville, Florida

+1 (904) 268.4000 Phone
+1 (904) 268.3197 Fax

Click here to email us

Web Solutions: Snug Creative

© 2024 Rezorect